前言：PC，PC2805，科思创2805，拜耳2805，PC科思创
物性表机械性能测试条件测试方法测试结果单位断裂伸长率ASTM D638/ISO 527＞50%拉伸模量ASTM D638/ISO 5272400kg/cm?(MPa)[Lb/in?]伸长率ASTM D638/ISO 527＞66%Charpy冲击强度ASTM D256/ISO 179Nkg·cm/cm(J/M)ft·lb/inIZOD 缺口冲击强度ASTM D256/ISO 17990kg·cm/cm(J/M)ft·lb/inASTM D256/ISO 17915kg·cm/cm(J/M)ft·lb/in光学性能测试条件测试方法测试结果单位透光率ASTM D1003/ISO 1346889%折射率ASTM D542/ISO 4891.586热性能测试条件测试方法测试结果单位燃烧性（率）UL94V-2热变形温度ASTM D648/ISO 75138℃（℉）ASTM D648/ISO 75125℃（℉）维卡软化点ASTM D1525/ISO R306145℃（℉）线性膨胀系数ASTM D696/ISO 113590.65mm/mm.℃电气性能测试条件测试方法测试结果单位表面电阻率ASTM D257/IEC 600931E16Ω介电常数ASTM D150/IEC 602503.1ASTM D150/IEC 602503.0介电损耗ASTM D150/IEC 602505ASTM D150/IEC 6025090耐电弧性ASTM D495/IEC 60112275体积电阻率ASTM D257/IEC 600931E14Ω.cm物性性能测试条件测试方法测试结果单位成型收缩率ASTM D9550.6-0.8%密度ASTM D792/ISO 11831.2熔融指数（流动系数）ASTM D1238/ISO 113310g/10min吸水率 23℃/24HASTM D570/ISO 620.30%